Automated Author ProfileAwanikumar P. Patil
Awanikumar P. Patil
Current S-Index
Sum of Dataset Indices for all datasets
Average Dataset Index per Dataset
Average Dataset Index per dataset
Total Datasets
Total datasets for this author
Average FAIR Score
Average FAIR Score per dataset
Total Citations
Total citations to the author's datasets
Total Mentions
Total mentions of the author's datasets
S-Index Interpretation
The S-Index (Sharing Index) is a comprehensive metric that represents the cumulative impact of all your datasets. It is calculated as the sum of Dataset Index scores across all your claimed datasets.
What it means:
- A higher S-index indicates greater overall impact of your datasets relative to typical datasets in their fields of research
- The S-Index grows as you add more datasets or as existing datasets gain more citations and mentions
- It provides a single number to track your research data impact over time
Current S-Index: 1.1 (sum of 2 datasets Dataset Index scores)
More information here.
S-Index Over Time
Cumulative Citations Over Time
Cumulative Mentions Over Time
Datasets
This study investigates the effect of dissimilar metal welding of low nickel stainless steel (SS) and 304 SS employing tungsten inert gas (TIG) welding process by using three different filler materials (316L, 308L and 310 SS). Microstructural, mechanical properties and corrosion behavior in 3.5% NaCl solution was studied. The microstructural investigation revealed the formation of δ-ferrite and γ-austenite in the weld (welded by 316L and 308L filler). The Higher δ-ferrite content was found more in 316L weld zone. Whereas samples welded by 310 SS filler showed the columnar structure in the weld zone. Relatively wider heat affected zone (HAZ) was measured on Cr-Mn SS side as compared to 304 SS side. Impact fracture surface of all the welded samples exhibited dimple appearance. Corrosion studies showed better pitting corrosion resistance in 316L SS welded sample due to the beneficial effect of δ-ferrite and also the addition of molybdenum (Mo). Electrochemical impedance spectroscopy (EIS) revealed higher polarization resistance (Rp) in 316L SS as compared to other fillers. Galvanic current density was found to be higher in Cr-Mn SS as compared to 304 SS when coupled with different welded samples.
Authors
- Ankur V. Bansod ;
- Awanikumar P. Patil ;
- Jagesvar Verma ;
- Sourabh Shukla
This study investigates the effect of dissimilar metal welding of low nickel stainless steel (SS) and 304 SS employing tungsten inert gas (TIG) welding process by using three different filler materials (316L, 308L and 310 SS). Microstructural, mechanical properties and corrosion behavior in 3.5% NaCl solution was studied. The microstructural investigation revealed the formation of δ-ferrite and γ-austenite in the weld (welded by 316L and 308L filler). The Higher δ-ferrite content was found more in 316L weld zone. Whereas samples welded by 310 SS filler showed the columnar structure in the weld zone. Relatively wider heat affected zone (HAZ) was measured on Cr-Mn SS side as compared to 304 SS side. Impact fracture surface of all the welded samples exhibited dimple appearance. Corrosion studies showed better pitting corrosion resistance in 316L SS welded sample due to the beneficial effect of δ-ferrite and also the addition of molybdenum (Mo). Electrochemical impedance spectroscopy (EIS) revealed higher polarization resistance (Rp) in 316L SS as compared to other fillers. Galvanic current density was found to be higher in Cr-Mn SS as compared to 304 SS when coupled with different welded samples.